Submerged Arc Welding Flux Sj501

• Customization: Available
• state: Granule
• pH: Neutral
• Model NO.: HFX-SJ501
• Melting Point: Non
• Chemical Composition: CaF₂=10%-30%
• Function: Remove Oxides, Protect Weld Metal, Make the Liquid Solder Flow
• Application: Submerged-arc Welding
• Manufacturing Method: Smelting
• Transport Package: Pallet
• Specification: 10-40 mesh
• Trademark: WELDBST
• Origin: P. R. C.
• HS Code: 38109000
• Production Capacity: 50000 Mt/Year

Product Description

        Acid agglomerated flux for welding of ordinary carbon, low alloy structure and boiler quality steel matching with suitable SAW wire(such as EL8, EM12, EM12K). The flux suitable for high speed welding and provides very good weld bead appearance and excellent slag detachability even with narrow groove and fillet welds. The other character of HFX-SJ501 is high anti-cracking and  anti-blowhole ability. Especially it is insensitive to oil, rust, scale and dirt on the surface to be welded. Most being used to double-side with single pass weld and fillet welds. As the consumption of the flux is very low, It it very economical.

       Flux type: Aluminium titanium
       Basicity index: 0.5-0.8
       Grain size: 2.0-0.28mm(10-60 meshes)
       Net weight: 25kg/bag
       Export markets: gloal

Compositions of fluxes (%)

SiO2+TiO2	MnO+AI2O3	CaF2	S	P
25-35	50-60	3-10	≤0.06	≤0.08

Typical mechanical properties of deposited metal

Wire matched	Yield Strength Ó s (MPa)	Tensile Strength Ó b (MPa)	Elongation δ 5%	AKV (J)
				20°C	0°C
H08A	≥330	415-550	≥22	≥50	≥27
H08MnA	≥400	480-650	≥22	≥50	≥27
EL12	≥330	415-550	≥22	-	≥27
EM12K	≥400	480-650	≥22	-	≥27

NOTICE:
        1. Before welding, fluxes should be baked for 2 hours at 300-350°C.
        2. Removal of rust, oil, water and impurities etc. in welding area.