Submerged Arc Welding Wire Em13K H10mnsi

Product Details
Customization: Available
Type: Rolling Wire
Material: Steel
Still deciding? Get samples of US$ 5/kg
Request Sample
Gold Member Since 2022

Suppliers with verified business licenses

Audited Supplier

Audited by an independent third-party inspection agency

Registered Capital
100000 RMB
Plant Area
<100 square meters
  • Submerged Arc Welding Wire Em13K H10mnsi
  • Submerged Arc Welding Wire Em13K H10mnsi
  • Submerged Arc Welding Wire Em13K H10mnsi
  • Submerged Arc Welding Wire Em13K H10mnsi
  • Submerged Arc Welding Wire Em13K H10mnsi
  • Submerged Arc Welding Wire Em13K H10mnsi
Find Similar Products

Basic Info.

Model NO.
EM13K H10MnSi
Flux Containing
Not Containing Flux
Extended Length
>20mm
Standard
Aws A5.17 Em13K
Transport Package
Carton, Drum
Specification
1.6-5.0mm
Trademark
WELDBST
Origin
China
HS Code
72173010
Production Capacity
50000mt/Year

Product Description

      EM13K is a kind of welding wire with appropriate manganese and silicon content, it matches with low manganese and low silicon type welding flux, insensitive to the rust on the base metal, it has excellent bead molding, excellent slag detach ability.

       Standard: AWS A5.17 EM13K
                       GT/T 5293 H10MnSi
                       ISO 14171-B-SU25
       Flux contanining:  not
       Diameter:  1.6mm, 2.0mm, 2.5mm, 3.2mm, 4.0mm,5.0mm
       Surface treatment:  copper coated
       Weight: 15kg, 25kg, 50kg, 250kg etc.
       Packing:  Plastic inside with carton
       Weave bag outside


Application:
       To use with flux SJ101, it can be applied both for high-speed welding steel plate of tensile strength 420 MPa and filling welding, it is widely used for welding boiler, pressure vessels, bridges, shipbuilding etc..

Chemical composition of wire (%)
Item C Mn Si S P Cr Ni Cu
Standard value ≤0.14 0.80-1.10 0.60-0.90 ≤0.035 ≤0.035 0.020 ≤0.30 ≤0.35
Sample value 0.089 0.98 0.67 0.023 0.032 0.015 0.034 0.11

Typical mechanical properties of deposited metal
Item Tensile Strength
Rm(Mpa)
Yield Strength
Rel or Rp0.2(Mpa)
Elongation
(%)
AKV Impact value
(J)(-20°C)
with flux SJ101 415~550 ≥330 ≥22 ≥27

NOTICE:
       1. Dry the flux at 350~400°C for1-2 hours before use, completely remove rust,oil and dirt from the groove surface prior to welding.
       2. Before welding, rust, water and impurities are to be removed from the welded surfaces of workplaces.

Submerged Arc Welding Wire Em13K H10mnsiSubmerged Arc Welding Wire Em13K H10mnsiOur services
1. Free sample is available
2. OEM service is available
3. High quality and professional service.
4. Much more competitive price.
5. On-time delivery

FAQ
1. Can you provide free sample for quality testing?
    -Yes, we can provide few quantity on free base.
2.  Do you accept small order ?
    -Yes.
3.  Do you accept OEM ?
    - Yes, we accept OEM packing on FCL base.
4.  Do you accept mix items in one container ?
   - Yes.
5.  Do you have inspection procedures for product?
   - Yes, we have Mill Test Report with each shipment
 

Send your message to this supplier

*From:
*To:
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now
Contact Supplier